unknownSun Mar 25, 2012 8:37 am
This is a full custom 145cm twin. Sandwich construction, full sublimation top sheet and base, 19oz biax fiberglass over a full wood core. Love this board, It came out way better than I expected. Wanted to keep this one, but it is sold. The colors in the graphics pop so nicely. The pictures don't even do it justice.
image no longer available
image no longer available
image no longer available
image no longer available
Thanks for checking out my photos. We will get picks of our thrid board up soon!
unknownSun Mar 25, 2012 4:57 pm
Beautiful! Did you say biax??? Did you mean triax?
unknownSun Mar 25, 2012 5:44 pm
Definately used 19oz biaxial fiberglass. We needed a flexible board for a novice all mountain board. Worked great!
unknownSun Mar 25, 2012 6:21 pm
I use biax on my pow boards. I like the flex that biax glass provides on a playful board. For serious freeriding triax is much better.
unknownSun Mar 25, 2012 8:50 pm
Are you guys putting it at 45 deg? If not, why not just use uni and save some weight?
unknownThu Mar 29, 2012 11:03 pm
We are using a 45 weave so that we can keep some torsional stiffness in the boards. I would think the weight difference would be very small between biax and uni. Your thoughts?
unknownFri Mar 30, 2012 3:12 pm
Ok if you're using it at a 45 that makes sense. I thought you might be using it 0/90, and the 90 fibers wouldn't be doing much but adding weight.